|Place of Origin:||CHINA|
|Certification:||CE | RoHS | GB/T19001-2016/ISO 9001:2015|
|Packaging Details:||Plastic Double Tube | Paper Box/pieces|
|Supply Ability:||20million pieces / year|
|Material:||Polyaspartic Resin Polymer + High-grade Pigments And Special Additives||Color:||Glitter | Bright|
|Shelf Life:||12 Months||Operation:||Easy To Operate By Caulking Gun|
RoHS Stone Bonding Fast Curing Material,
No Sagging Bonding Fast Curing Material,
No Crack Stone Bonding Adhesive
Perflex Epro P-80 stone bond adhesive is a bi-component epoxy adhesive, made of high-tech polymer epoxy resin, hardener, high-grade pigments and additives.
It is pre-dosed automatically thanks to the cartridge where it is packaged. Part A and part B are located in two separate pipes, using the special nozzle-mixer together with the caulking gun with two pistons, the correct dosage of the components is obtained.
Regular polish and matt colors series are available.
COLOR AVAILABLE - 18 COLORS
1. After the mortar solidified, the joint of marble, tile, stone, etc must be cleaned, dried.
2. Use cleaning wax on both sides of the joint beforehand, pay attention not to wipe wax into the gap.
3. Twist the tube cap, install it on the head of the double-tube sealant, cut the spiral rubber nozzle obliquely at the head by 45 degrees (the opening size depends on the size of the tile seam), and then install it in the caulking gun.
4. Extrude about 20 cm colloid (in order to mix it fully and remove bubbles), then inject the glue into the joint that should be bonded
5. Press the ready glue on the joint surface with with the pressing plate.
6. After 3-6 hours (depending on the temperature), the glue cures completely, scrape off the excess glue on both sides of the gap with a scraper.
PREBOND P-80 is developed for bonding marble, stone, granite, quartz and ceramic, for external and internal use.
|Testing Item||Resin A||Hardener B|
|Appearance||Semi-fluid liquid||Thixotropic paste|
|Blend Ratio(by volume)||A : B = 1 : 1|
|Chromatic Aberration △E||≤1.5|
|Working time(25℃*min)||40 ± 5 min|
|Gel time in bulk (25℃*min)||20 ± 5 min|
|Colloidal fluidity after blending||Thixotropic fluid|
|Wear Resistance (750 g.500 r)/g||0.030|
|Sagging after blending||No sagging|
|Tensile Shear Strength/MPa||Standard condition||≥5.0|
|High/low temperature switch.||≥3.0|
|Water absorbent 25℃24 hour(%)||＜0.2|
|Waterproof / 24h||No change|
|Chemical Resistance / 2h||No change|
|Stain Resistance (Vinegar, soy, oil)/ 1h||No change|
Testing condition: 21-25℃,relative humidity 45-55%. Constructed by caulking gun.