High Wear Resistance Micro Bead Polyaspartic Floor Coating

High Wear Resistance Micro Bead Polyaspartic Floor Coating

  • High Wear Resistance Micro Bead Polyaspartic Floor Coating
High Wear Resistance Micro Bead Polyaspartic Floor Coating
Product Details:
Brand Name: PERFLEX
Certification: CE/ROHS/ISO9001
Model Number: PXF-500 / SIKA 315
Payment & Shipping Terms:
Minimum Order Quantity: 200 pails
Packaging Details: 5 L/10L/20L per pail
Delivery Time: 7days around
Supply Ability: 20000 Ton annually
Contact Now
Detailed Product Description
MATERIAL: Polyaspartic Resin + Isocyanate Hardener Blend Ratio: A : B : C= 100 : 20 : 50
Color: Transparent Feature: Good Bonding | Weather Resistance
Package: 5L | 10L | 20L / Pail Application: Park | Road | Garden | Swimming Pool Flooring
High Light:

Micro Bead Polyaspartic Floor Coating

,

High Wear Resistance Polyaspartic Floor Coating

,

Micro Bead Polyaspartic Coating

PXF-500 High Wear Resistance Polyasartic Flooring Coating - Micro Bead | weather resistance | Ultra clear

 

 

INTRODUCTION: PXF-500 is a three-component reaction curing transparent floor coat made of polyaspartic resin, HDI hardener and organic micro bead materials, with sepcial organic micro bead and multi-functional chemical, it can provide strong adhesion and substrate adhesion when overcoat on epoxy or polyurethane substrate, and super wear and scratch resistance of the coating layer. It’s has good anti- QUV properties, anti-aging and yellowing resistance and chemical resistance performance, the best choice for heavy duty vehicle flooring indoor or outdoor. 

 

FEATURE

1- Low maintenance
2- Excellent UV resistance
3- Low VOC-content, low odor
4- Durable, impermeable and seamless
5- Smooth glossy finish, optional slip resistant semi-gloss
 finish
6- Unique UV blocker technology provides superior
 ultraviolet light screening

High Wear Resistance Micro Bead Polyaspartic Floor Coating 0

APPLICATION: Typically used in light to heavy-duty traffic areas

 

▪ Laboratories, Life Sciences, Pharmaceutical industries and Health Care industry.
▪ Education (e.g. Schools and Universities).
▪ Leisure & Culture (e.g. Museums, Stadiums).
▪ Retail (e.g. Shopping Malls).
▪ Manufacturing facilities and warehouses.

 

PHYSICAL PROPERTIES 

 

Part A Resin Part B Hardener
Appearance Transparent Appearance  Transparent
Viscosity 25 ℃ 1200mpas Viscosity 25 ℃ 12mpas
Specific gravity 25 ℃ 1.15 Specific gravity 25 ℃  
Solid content 99% Solid content  

 

Part D: Organic Micro Bead Materials

 

PROPERTIES AFTER CURING

7-day hardness Shore D 68
Abrasion (CS17 wheel 750g, 500r) / Mg 25
Elongation at break (%) 15
Tensile strength (MPA) 23
Concrete adhesion (MPA) 2.2
Acid resistance no change in 5% sulfuric acid
Alkali resistance no change in 10% sodium hydroxide
Impact resistance (1000g, 1m) Pass

 

 

CONSTRUCTION PARAMETERS 

 

- BLEND RATIO BY WEIGHT
 A :  B : D = 100 : 20 : 50
 

 - WORKING TIME

Temperature (℃) 25 30  
Mixed service life (min) 20 15  

 

- CONSTRUCTION CONDITIONS 
 

Construction amount: strictly control the amount in 0.05 ~ 0.1kg/m2 to avoid accumulation, otherwise the foaming is serious
Construction conditions:
Ambient temperature: 0 ℃ - 35 ℃, ambient humidity: ≤ 85%
Substrate temperature: must be more than 3 ℃ above air dew point temperature
Cleaning agent: Asparagus polyurea standard diluent
Note: this material has very high requirements for construction, and can only be operated after professional training of our company before use.

 

- DRY TIME AND RECOAT INTERVAL
Temperature (℃) : 25
Walking opening hours (HRS): 8
Vehicle opening hours (HRS) : 2

Recoat interval hours (HRS): 2

The above data is only for guidance, and the real curing time is highly related to the ambient temperature and humidity.

 

- SURFACE TREATMENT
Clean water to remove salt and other water-soluble contaminants.
Use proper detergent and degreaser to remove grease.
Clean and dry the surface before construction.
Pay attention to the painting interval between the primer and the construction.

 

STORAGE


Storage time: 12 months
Storage temperature: 5 ℃ - 35 ℃

 

PACKAGE


Part A: 3kg  |  Part B: 0.6kg | Part D: 1.4kg

 

Contact Details
CHANGSHA PERFLEX NOVEL MATERIALS CO.,LTD

Contact Person: Laura

Send your inquiry directly to us (0 / 3000)

Other Products

Contact

Address: Changsha . Hunan China

Factory Address:Baofeng Industrial Zone, Shashi County, Liuyang Changsha City, Hunan China