|Minimum Order Quantity:||200 pails|
|Packaging Details:||5 L/10L/20L per pail|
|Delivery Time:||7days around|
|Supply Ability:||20000 Ton annually|
|MATERIAL:||Polyaspartic Resin + Isocyanate Hardener||Blend Ratio:||A : B = 1 : 1|
|Color:||Transparent Or Pigmented||Feature:||Good Bonding | Weather Resistance|
|Package:||10L / Pail||Application:||Park | Road | Garden | Swimming Pool Flooring|
Polyaspartic Floor Coating 10KG,
Seamless Polyaspartic Floor Coating,
Weather Resistance Polyaspartic Floor Coating
PXF-100 Seamless Flooring Topcoat 10KG - Flake Floor | Scratch resistance | weather resistance | Ultra clear
INTRODUCTION: PF-100 is a two-component reaction curing transparent floor coat made of polyaspartic resin and HDI hardener, with interpenetrating structure and multi-functional chemist bonding, it can provide strong adhesion and substrate adhesion for permeable floor layer. Chemical toughening and modification can give the cured good flexibility, effectively avoid the excessive brittleness of traditional adhesive, effectively absorb the stress from the ground materials, and form a certain degree of rigid flexible Island effect, it’s has good anti- QUV properties, anti-aging and yellowing resistance.
APPLICATION: floor decoration for school classrooms, high-end offices, super market, hotel lobby, airport, restaurant, showroom, etc.
FEATURE: The process of permeable stone flooring is to bond stone with adhesive by "point bonding", that requires the adhesive must has high adhesion, weather resistance, acid and alkali resistance, water erosion resistance, wear resistance and impact resistance.
1- Overall beautiful decoration, antiskid surface effect.
2- Quick curing, short construction period, and the construction is much simpler than epoxy grindstone.
3- Excellent cracking resistance, super weather resistance, non yellowing, no pulverization, indoor and outdoor use.
2- Strong and tough adhesion, ultra-clear, high gloss, wetting effect on color aggregate without changing the flake/quartz primary color.
4- Rich color, color can be ultra-clear or being customized.
5- High solid content, low VOC.
|Part A||Resin||Part B||Hardener|
|Viscosity 25 ℃||400mpas||Viscosity 25 ℃||100mpas|
|Specific gravity 25 ℃||1.02||Specific gravity 25 ℃||1.01|
|Solid content||90%||Solid content||64%|
PROPERTIES AFTER CURING
|7-day hardness||Shore D 68|
|Abrasion (CS17 wheel 750g, 500r) / Mg||25|
|Elongation at break (%)||15|
|Tensile strength (MPA)||23|
|Concrete adhesion (MPA)||2.2|
|Acid resistance||no change in 5% sulfuric acid|
|Alkali resistance||no change in 10% sodium hydroxide|
|Impact resistance (1000g, 1m)||Pass|
- BLEND RATIO
A : B = 1 :1
- WORKING TIME
|Mixed service life (min)||40||30||20|
- CONSTRUCTION CONDITIONS
Ambient temperature: 0 ℃ - 35 ℃, ambient humidity: ≤ 85%
Substrate temperature: must be more than 3 ℃ above the air dew point temperature
Cleaning agent: standard diluent of polyaspartic
- DRY TIME AND RECOAT INTERVAL
Temperature (℃) : 25
Walking opening hours (HRS): 3
Vehicle opening hours (HRS) : 7
Recoat interval hours (HRS): 3
The above data is only for guidance, and the real curing time is highly related to the ambient temperature and humidity.
Paint: 10L | Curing agent: 10L
1 - Preparation of colored stone aggregate
2- Stone aggregate & adhesive mixing
3- Dumping and spreading
4- Stone aggregate spreading
5-Trimming and troweling
6- Waiting for forming
Tools: small mixer, mud bucket, grinder, knife
Flack or Quartz Aggregate : according to the color type and stone size selected by customers.