Premium Waterproof Floor Tile Grout Polyaspartic Material Environment Friendly

^{Polyaspartic is premium anti-corrision and waterproof materials, usually polyaspartic materials applys in concrete and metal surface protecion udner terrible enviroment like windmill, heavy duty machine, offshore platform, rail concrete protection, swimming pool and roof waterproof, etc. It has super adhesion to tiles, ceramic tile, marble.}

 

Part 1 Testing Result of Polyaspartic Grout & Epoxy Grout

 

No	Testing Item		Polyaspartic Grout	Epoxy Grout	Testing Method
1	Solid Content%		＞95	＞95	105℃,2hr
2	Odor		Odorless	Odorless
3	Operability		Good	Good	By glue gun
4	Appearance		Good	Good	By visual
5	Gluing time min		20	60
6	Press time min		15	60
7	Tack free hour		1	2hr	Finger touch method
8	Scraping time hour		＞3	＞6
9	Anti-yellowing		Good	Bad	UV-A Aging
10	Hardness shore D		70	80	Shore D
11	Flexibility(6 days)		Good	Good	1mm bend
12	Flexibility(UVA 6 days)		Good	Bad	1mm bend
Remark: room temperature 23℃,70%RH environment maintain test.

 

Part 2 Flexibility Testing by Different Time

 

Flexibility testing method:paint 0.5mm on Tinplate, observe whether crack after bending. As shown in the figure, the result after 1mm film bending at room temperature 20℃70%RH maintain.

 

Maintain time	Epoxy Grout	Polyaspartic Grout
20hr	Cracking seriously	Cracking slightly
2 days	Cracking seriously	No cracking
5 days	Cracking seriously	No cracking
10 days	Cracking seriously	No cracking

 

Result: As epoxy has no flexibility, 10 days later it’s cracking seriously after bending. After completely cured after 3days, polyaspartic flexibility is super good, no crack at all.

 

Part 3 QUV Aging Testing, Anti-yellowing Testing

 

 

             

1.  
2. After 1 day QUVa raying, epoxy grout is yellowing seriously, however polyaspartic grout has no change by visual.
3. After 1 day QUVa raying, epoxy grout is peeling off, after 5days, the situation is even worse, finally the grout is cracking and dropping off, however polyaspartic is still good bounding.
4. Epoxy grout is aging and losing gloss seriously(99→30), however polyaspartic grout gloss is stable.(91→89.4).

 

Part 4 Adhesion Testing

 

 

Result: the adhesion of epoxy grout and polyaspartic grout on substrate is good after original QUVa raying, along with the longer raying time, the epoxy grout aging speed is accelerated and chalking, shrinking seriously, result in cracking and peeling off. However, polyaspartic grout performance well,no obvious change.

 

 

 

^{1- Super weather resistance and QUV resistance, the grout outdoor under the sunshine won't be chalking and the color won't be fading and yellowing forever.}

^{2- Slightly elastic film that can endure more terrible temperature sticking firmly in the}

^{ceramic tile seam, which avoid the grout peeling off and crack.}

^{3- Made of polyaspartic materials, it can be cured itself under the pretty low temperature even minus 35 degree, therefore P-30 is a products that do not being affected by temperature.}

 

^{In addition, Polyaspartic Tile Grout P-30 has all features as epoxy tile grout P-20, like it has high bonding strength, excellent physical properties such as non-sagging, tear/scratch/wear resistance. After curing, it is super anti-mildew, anti-bacterial, stain resistance, waterproof, moisture-proof, colorful, durable, smooth as porcelain, hard as diamond, bright as crystal, easy to clean, etc. The construction is very simple and convenient.}

 

  

^{GOOD BOINDING TO VARIOUS TILE&STONE}

 

^{Perflex Polyaspartic Tile Grout P-30 is suitable for bonding, filling and beautifying the joint of ceramic tile, marble and stone building materials such as ceramic tile floor, ceramic tile wall, washbasin, bathtub, toilet, kitchen table, door-crossing stone, etc. Especially because of super weather resistance, P-30 is the best choice for balcony, roof, etc outdoor grouting.}

 

 

^{1. After the mortar solidified, the ceramic tile crevice must be cleaned, the impurities and dust in the ceramic tile crevice must be cleaned up with wallpaper knife and vacuum cleaner.}

^{2. Use cleaning wax on both sides of the gap beforehand with proper amount, pay attention not to wipe wax into the gap.}

^{3. Twist the tube cap, install it on the head of the double-tube sealant, cut the spiral rubber nozzle obliquely at the head by 45 degrees (the opening size depends on the size of the tile seam), and then install it in the rubber gun.}

^{4. Extrude about 20 cm colloid (in order to mix it fully and remove bubbles), then inject the glue into the crevice of ceramic tile.}

^{5. Press the ready glue on the crevice with with the seam press or steel bal.}

^{6. After 4-24 hours (depending on the temperature), the glue cures completely, scrape off the excess glue on both sides of the gap with a scraper.}

 

                          

 

 

^{400ml per plastic cartridge, 20 Cartridge per carton.}

     

 

^{12 months if the product is stored in a dry and cool place away from light.}