WHY POLYASPARTIC TILE GROUT P-30 IS PRIOR TO EPOXY GROUT - Testing Report
Polyaspartic is premium anti-corrision and waterproof materials, usually polyaspartic materials applys in concrete and metal surface protecion udner terrible enviroment like windmill, heavy duty machine, offshore platform, rail concrete protection, swimming pool and roof waterproof, etc. It has super adhesion to tiles, ceramic tile, marble.
Part 1 Testing Result of Polyaspartic Grout & Epoxy Grout
No | Testing Item | Polyaspartic Grout | Epoxy Grout | Testing Method | |
1 | Solid Content% | >95 | >95 | 105℃,2hr | |
2 | Odor | Odorless | Odorless | ||
3 | Operability | Good | Good | By glue gun | |
4 | Appearance | Good | Good | By visual | |
5 | Gluing time min | 20 | 60 | ||
6 | Press time min | 15 | 60 | ||
7 | Tack free hour | 1 | 2hr | Finger touch method | |
8 | Scraping time hour | >3 | >6 | ||
9 | Anti-yellowing | Good | Bad | UV-A Aging | |
10 | Hardness shore D | 70 | 80 | Shore D | |
11 | Flexibility(6 days) | Good | Good | 1mm bend | |
12 | Flexibility(UVA 6 days) | Good | Bad | 1mm bend | |
Remark: room temperature 23℃,70%RH environment maintain test. |
Part 2 Flexibility Testing by Different Time
Flexibility testing method:paint 0.5mm on Tinplate, observe whether crack after bending. As shown in the figure, the result after 1mm film bending at room temperature 20℃70%RH maintain.
Maintain time | Epoxy Grout | Polyaspartic Grout |
20hr | Cracking seriously | Cracking slightly |
2 days | Cracking seriously | No cracking |
5 days | Cracking seriously | No cracking |
10 days | Cracking seriously | No cracking |
Result: As epoxy has no flexibility, 10 days later it’s cracking seriously after bending. After completely cured after 3days, polyaspartic flexibility is super good, no crack at all.
Part 3 QUV Aging Testing, Anti-yellowing Testing
1- After 1 day QUVa raying, epoxy grout is yellowing seriously, however polyaspartic grout has no change by visual.
2- After 1 day QUVa raying, epoxy grout is peeling off, after 5days, the situation is even worse, finally the grout is cracking and dropping off, however polyaspartic is still good bounding.
3- Epoxy grout is aging and losing gloss seriously(99→30), however polyaspartic grout gloss is stable.(91→89.4).